Jung, V.; Heinemeyer, F.; Köntges, M.: Long-term stable encapsulated solder joints on an Al/Ni:V/Ag metallization for silicon solar cells. In: Energy Procedia 21 (2011), S. 84-91. DOI: https://doi.org/10.1016/j.egypro.2012.05.011
Zusammenfassung: | |
Evaporated Al as metallization for silicon solar cells may be profitable as it requires less Al material than the common screen-printed Al/Ag-paste combinations and forms contacts with a lower contact resistivity. To achieve solderability a sputter deposited Ni:V and an Ag layer are deposited onto the evaporated Al layer. Tin-coated Cuconnectors with a lead-free and a lead-containing solder are employed in combination with two halogen-free no-clean fluxes with varying solid contents. The long-term solderability of the metallization stack is demonstrated by comparing 180° peel forces (DIN EN 50461) of Cu-connectors soldered onto the metallization stack directly after preparation, after accelerated storing following IPC J-STD-003B and after storing for half a year at room temperature. The long-term stability of the solder joints is verified by measuring the normalized contact resistivity and by a visual inspection of encapsulated samples during a damp heat test (DIN EN 61215). For encapsulation an EVA foil and a silicone elastomer are used as encapsulation materials. As the lead-containing solder does not adhere sufficiently after accelerated aging, the flux with high contend of solids may accelerate corrosion and the EVA laminates exhibit adhesion problems between the samples and the lamination foil. The lead-free solder and the flux with the lower solid content in a silicone elastomer based laminate emerge to be the most promising candidates for a long term stable interconnection of Al/Ni:V/Ag metallized solar cells. | |
Lizenzbestimmungen: | CC BY-NC-ND 3.0 Unported |
Publikationstyp: | Article |
Publikationsstatus: | publishedVersion |
Erstveröffentlichung: | 2011 |
Die Publikation erscheint in Sammlung(en): | An-Institute |
Pos. | Land | Downloads | ||
---|---|---|---|---|
Anzahl | Proz. | |||
1 | Germany | 56 | 42,75% | |
2 | United States | 41 | 31,30% | |
3 | China | 14 | 10,69% | |
4 | Honduras | 5 | 3,82% | |
5 | Vietnam | 2 | 1,53% | |
6 | Israel | 2 | 1,53% | |
7 | Canada | 2 | 1,53% | |
8 | Latvia | 1 | 0,76% | |
9 | Iran, Islamic Republic of | 1 | 0,76% | |
10 | Czech Republic | 1 | 0,76% | |
andere | 6 | 4,58% |
Hinweis
Zur Erhebung der Downloadstatistiken kommen entsprechend dem „COUNTER Code of Practice for e-Resources“ international anerkannte Regeln und Normen zur Anwendung. COUNTER ist eine internationale Non-Profit-Organisation, in der Bibliotheksverbände, Datenbankanbieter und Verlage gemeinsam an Standards zur Erhebung, Speicherung und Verarbeitung von Nutzungsdaten elektronischer Ressourcen arbeiten, welche so Objektivität und Vergleichbarkeit gewährleisten sollen. Es werden hierbei ausschließlich Zugriffe auf die entsprechenden Volltexte ausgewertet, keine Aufrufe der Website an sich.