Just, G.; Koch, I.; Brod, M.; Jansen, E.; Gude, M. et al.: Influence of reversed fatigue loading on damage evolution of cross-ply carbon fibre composites. In: Materials 12 (2019), Nr. 7, 1153. DOI: https://doi.org/10.3390/ma12071153
Zusammenfassung: | |
Microcrack formation and delamination growth are the main damage mechanisms in the fatigue of composites. They lead to significant stiffness loss, introduce stress concentrations and can be the origin of subsequent damage events like buckling or fibre breakage, especially in case of shear and compression stresses during load reversal. Fatigue experiments of carbon fibre reinforced laminates were conducted at several stress ratios and analysed in terms of crack and delamination growth. These investigations were accompanied by microscopic imaging, digital image correlation and finite element modelling to take into account the effects of residual stresses and crack closure. It was found that residual stresses significantly change the local stress ratio in off-axis layers and lead to residual crack opening of inter fibre cracks. These cracks remain open and close under high compression loadings only. Furthermore, crack formation under pulsating compression loading turned out to be driven by residual stresses leading to perpendicular cracks as observed under pure tension loading. The experimental findings further confirm the severe detrimental effect of tension-compression loading on crack formation and delamination growth compared to pulsating tension-tension or compression-compression loads. | |
Lizenzbestimmungen: | CC BY 4.0 Unported |
Publikationstyp: | Article |
Publikationsstatus: | publishedVersion |
Erstveröffentlichung: | 2019 |
Die Publikation erscheint in Sammlung(en): | Fakultät für Bauingenieurwesen und Geodäsie |
Pos. | Land | Downloads | ||
---|---|---|---|---|
Anzahl | Proz. | |||
1 | Germany | 50 | 57,47% | |
2 | United States | 24 | 27,59% | |
3 | China | 4 | 4,60% | |
4 | Russian Federation | 2 | 2,30% | |
5 | United Kingdom | 2 | 2,30% | |
6 | No geo information available | 1 | 1,15% | |
7 | Taiwan | 1 | 1,15% | |
8 | Netherlands | 1 | 1,15% | |
9 | Iran, Islamic Republic of | 1 | 1,15% | |
10 | Indonesia | 1 | 1,15% |
Hinweis
Zur Erhebung der Downloadstatistiken kommen entsprechend dem „COUNTER Code of Practice for e-Resources“ international anerkannte Regeln und Normen zur Anwendung. COUNTER ist eine internationale Non-Profit-Organisation, in der Bibliotheksverbände, Datenbankanbieter und Verlage gemeinsam an Standards zur Erhebung, Speicherung und Verarbeitung von Nutzungsdaten elektronischer Ressourcen arbeiten, welche so Objektivität und Vergleichbarkeit gewährleisten sollen. Es werden hierbei ausschließlich Zugriffe auf die entsprechenden Volltexte ausgewertet, keine Aufrufe der Website an sich.