Behrens, Bernd-Arno; Yilkiran, Deniz; Schöler, Simon; Özkaya, Fahrettin; Hübner, Sven et al.: Wear investigation of selective α-Fe2O3 oxide layers generated on surfaces for dry sheet metal forming. In: Procedia Manufacturing 15 (2018), S. 923-930. DOI:
https://doi.org/10.1016/j.promfg.2018.07.404
Zusammenfassung: |
To realize a dry sheet metal forming process, α-Fe 2 O 3 oxide layers were investigated regarding their friction characteristics, wear behavior and surface energy depending on different surface qualities of the specimens examined. The oxide layers were generated in a new hybrid batch furnace. The layer generation on all specimens of the tool steel 1.2379 used was performed at a target temperature below the annealing temperature (≈ 510 °C). Friction coefficients were examined with plane strip drawing tests. Wear experiments with oxidized wear specimens with variable surface topographies were carried out up to several thousand strokes per surface condition.
|
Lizenzbestimmungen: |
CC BY-NC-ND 4.0 Unported - https://creativecommons.org/licenses/by-nc-nd/4.0/
|
Publikationstyp: |
Article |
Publikationsstatus: |
publishedVersion |
Erstveröffentlichung: |
2018 |
Schlagwörter (englisch): |
Forming processes, Composite material, Materials science, Surface energy, Tool steel, Sheet metal, Oxide, Annealing (metallurgy)
|
Fachliche Zuordnung (DDC): |
620 | Ingenieurwissenschaften und Maschinenbau
|
Kontrollierte Schlagwörter: |
Konferenzschrift
|